（完整版）水性油墨用水性聚氨酯的合成与研究毕业设计

`

水性油墨用水性聚氨酯的合成与研究

Synthesis and research of waterborne polyurethane for application in water-based ink

binder

目 录

摘要 ..........................................................

Abstract ......................................................

引言 ..........................................................

第一章 绪 论 ..................................................

1.1概述 .............................................................

1.2水性聚氨酯发展概况 ...............................................

1.2.1水性聚氨酯国内发展概况 .........................................

1.2.2水性聚氨酯国外发展概况 .........................................

1.3水性聚氨酯的分类 .................................................

1.3.1以外观划分 .....................................................

1.3.2以亲水性基团的性质划分 .........................................

1.3.3以聚氨酯原料划分 ...............................................

1.4水性聚氨酯的制备方法 .............................................

1.4.1自乳化法和外乳化法 .............................................

1.4.2预聚体法和丙酮法 ...............................................

1.5水性聚氨酯制备用主要原料 .........................................

1.5.1低聚物多元醇 ...................................................

1.5.2异氰酸酯 .......................................................

1.5.3扩链剂 .........................................................

1.5.4亲水性扩链剂 ...................................................

1.6水性油墨用水性聚氨酯的发展趋势 ...................................

1.7本文研究的目标、主要内容及意义 ...................................

第二章 水性油墨用水性聚氨酯分散体的合成 ........................

2.1概述 .............................................................

2.2实验药品与仪器 ...................................................

2.2.1实验药品 .......................................................

2.2.2实验仪器 .......................................................

2.2.3合成工艺 .......................................................

2.2.4乳胶膜的制备 ...................................................

2.3产物表征与性能测试 ...............................................

2.3.1成膜外观与透明度 ...............................................

2.3.2红外光谱分析（IR） .............................................

2.3.3乳液固含量的测定 ...............................................

2.3.4乳液粘度的测定 .................................................

2.3.5乳液pH值的测定 ................................................

2.3.6乳液酸值的测定 .................................................

2.3.7 TG测试 ........................................................

2.3.8乳液粒径与Zeta电位的测试 ......................................

2.3.9凝胶渗透色谱分析GPC ............................................

2.3.10 X-ray衍射(XRD)实验 ...........................................

2.4结果与讨论 .......................................................

2.4.1水性聚氨酯分散液的性能 .........................................

2.4.2 TG热失重测试与结果分析 ........................................

2.4.3粒径测试与Zeta电位测定 ......................... 错误！未定义书

2.4.4红外分析结果 ...................................................

2.4.5 GPC分析结果 .................................... 错误！未定义书

2.4.6 XRD分析结果 .................................... 错误！未定义书

结 论 ........................................... 错误！未定义书

致 谢 ........................................... 错误！未定义书

参考文献 ......................................... 错误！未定义书

水性油墨用水性聚氨酯的合成与研究

摘要：本文采用分子质量为2000的聚氧化丙烯二醇（PPG）、异佛尔酮二异氰酸酯(IPDI)、二羟甲基丙酸(DMPA)、三乙胺(TEA)、二月桂酸二丁基锡(DBTDL)、1,4- 丁二醇(BDO )、N-甲基-2-吡咯烷酮（NMP）和丁酮（MEK）为原料并通过预聚体法制成四种软硬段摩尔比不同的水性聚氨酯分散体样品PU3、PU4、PU5、PU6, 测量了它们的固含量、粘度、pH值、酸值、粒径分布及Zeta电位等对其性能进行研究，并采用红外光谱（FTIR）、凝胶渗透色谱（GPC）、热失重（TG）以及X-ray粉末衍射（XRD）分析表征合成产物。结果表明，合成的水性聚氨酯乳液属于纳米级并且具有微弱的结晶性，其中平均粒径为56.4nm，Zeta电位值为-92.2mV，分散系数为4.314的PU4乳液样品热稳定性最好，适合用于水性油墨。 关键词：水性聚氨酯；软硬段比值；水性油墨；纳米级