德兴铜矿辉钼矿精矿的选择性电氧化浸出与分离过程

第 23 卷第 8 期 Vol.23 No.8 

中国有色金属学报 

The Chinese Journal of Nonferrous Metals 

2013 年 8 月 Aug. 2013 

文章编号：1004­0609(2013)08­2290­06 

德兴铜矿辉钼矿精矿的选择性电氧化浸出与分离过程

曹占芳 1,2,3 ，钟 宏 1, 3 ，姜 涛 2 ，刘广义 1,3 ，王 帅 1, 3 

(1. 中南大学 化学化工学院，长沙 410083； 2. 中南大学 资源加工与生物工程学院，长沙 410083； 3. 中南大学 有色资源化学教育部重点实验室，长沙 410083) 

摘 要：针对德兴铜矿高铜钼精矿特性，研究开发一种选择性电氧化浸出新工艺。结果表明，辉钼矿的电氧化浸 出受电解液 pH 值的影响显著。采用 Na2CO3­NH4HCO3 缓冲溶液控制电解过程 pH 为 9 左右，可以实现辉钼矿的 选择性电氧化高效浸出，钼、铼的浸出率分别为 99.35%和 99.79%，与非缓冲体系的电氧化过程相比，钼、铼的 浸出率分别提高了 23.86%和 26.50%。在选择性电氧化过程中，黄铜矿基本上不能浸出而留在浸出渣中，电解渣 中铜品位达到 10.84%，回收率达到 97.93%，可作为铜冶炼原料而回收。采用 N235 为萃取剂，对电氧化浸出液 中的钼、铼进行溶剂萃取，将溶液中 HCl浓度调整为 25.48 g/L时，可实现钼、铼的同时萃取，其萃取率分别为 99.84%和95.19%；用17%的氨水反萃负载有机相，有机相中钼、铼的反萃率分别为99.89%和99.54%。将反萃液 pH调整为8，30℃下用D201树脂吸附1 h，钼、铼的吸附率分别为3.46%和92.18%，分离因子为169.56。 关键词：辉钼矿；电氧化；萃取；吸附 中图分类号：TF111 

文献标志码：A 

Selective electric­oxidation leaching and separation of 

Dexing molybdenite concentrates 

1, 2, 3 1, 3 2 1, 3 1, 3 

CAO Zhan­fang , ZHONG Hong , JIANG Tao , LIU Guang­yi , WANG Shuai 

(1.School of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China  2.School of Minerals Processingand Bioengineering, Central South University, Changsha410083, China  3.Key Laboratory of Resources Chemistry of Nonferrous Metals,Central South University, Changsha 410083, China) Abstract: A novel technique of selective electric­oxidation leaching, solvent extraction and ion exchange adsorption was studied for the recovery of Dexing molybdenite concentrates. The results show that the electric­oxidation leaching of molybdenite is impacted evidently bypH value of electrolyte. When the pH of electric­oxidation process wasadjusted by buffered solutions of sodium carbonate and ammonium acid carbonate to about 9, MoS2 and ReS2 could be selectively oxidized, the dissolution rates of molybdenite and rhenium are 99.35% and 99.79%, respectively. Compared with that of theunbuffered system, the dissolution rates of molybdenite and rhenium increaseby23.86% and 26.50%,respectively. In the process of selective electric­oxidation leaching, chalcopyrite would not be leached, the grade of copper in the residue is 10.84% with a recovery rate of 97.93%, and it can be used as copper smelting materials. The separation of molybdenum and rhenium in the electrolyte was studied by solvent extraction and D201 resinadsorption. Coextraction of molybdenum and rhenium is found when N235 was used as an extractant and the concentration of HCl was adjusted to 25.48 g/L, the extraction efficiencies of Mo(Ⅵ) and Re(Ⅶ) are 99.84% and 95.19%, respectively. The stripping of molybdenum and rhenium to aqueous phase was investigated using 17% ammonia liquor, the stripping efficiencies of 

基金项目：国家自然科学基金资助项目 (21106188)； 湖南省自然科学基金项目(12JJ4013)； 中国博士后科学基金资助项目(2011M501299, 2012T50709)；

中南大学中央高校基本科研业务费专项资金资助项目(2011QNZT050) 

收稿日期：2012­02­11；修订日期：2013­05­20 

通信作者：钟 宏，教授，博士；电话：0731­88830603；传真：+86 731­88879616；E­mail: zhongh@http://doc.guandang.net

第 23 卷第 8 期 曹占芳，等：德兴铜矿辉钼矿精矿的选择性电氧化浸出与分离过程 2291 

Mo(Ⅵ) and Re(Ⅶ) are about 99.89% and 99.54%, respectively. After stripping, rhenium was separated from molybdenum using D201 resin under pH 8 at 30℃, the adsorption rates of rhenium and molybdenumare 92.18%, 3.46%, respectively, and the separating factor is 169.56. …… 此处隐藏：10482字，全部文档内容请下载后查看。喜欢就下载吧 ……